Toothpaste Grade CMC is a high-purity carboxymethyl cellulose product designed for toothpaste, gels, and whitening paste formulations. It works as a binder, thickener, and stabilizer, helping improve texture, viscosity consistency, abrasive dispersion, formulation stability, and brushing experience.
| Quantity: | |
|---|---|
Sentai’s toothpaste-grade CMC is a high-purity cellulose derivative engineered to deliver exceptional thickening, binding, and stabilizing performance in oral care products. With ultra-low impurities and strict compliance with global safety standards, it ensures superior texture, stability, and user experience in toothpaste, gels, and whitening pastes.
✅ Optimal Rheology Control
• Creates smooth, non-stringy textures with consistent viscosity (adjustable 800–5,000 mPa·s).
• Prevents phase separation and ensures uniform dispersion of abrasives (e.g., silica) and actives (e.g., fluoride).
✅ Enhanced Stability
• pH-resistant (4.0–10.0): Maintains performance in fluoride, whitening, or herbal formulations.
• Salt-tolerant: Compatible with potassium nitrate (sensitivity relief) and zinc citrate (anti-tartar agents).
✅ Superior Mouthfeel
• Delivers a creamy, non-gritty texture for premium brushing experience.
• Improves foam structure without compromising rinseability.
✅ Clean-Label Compatibility
• Non-GMO & Vegan-friendly: Replaces synthetic thickeners (e.g., carbomer).
• Biodegradable: Red environmental footprint.
Parameter | Specification |
Appearance | Ultra-fine white powder |
Purity | ≥99.5% (heavy metals ≤10 ppm) |
Viscosity (1% sol.) | 800–5,000 mPa·s (customizable) |
Moisture | ≤8% |
pH (1% solution) | 6.5–8.5 |
Particle Size | 95% through 200 mesh |
• Recommended Dosage: 0.8–1.5% of total formulation.
• Process: Disperses instantly in water/glycerin base; hydrate at 40–50°C for full viscosity development.
• Synergies: Works seamlessly with sorbitol, xanthan gum, and carrageenan.
Elevate Your Oral Care Line with Sentai!
Contact us for samples, technical data sheets, and formulation support.